Chiusura uffici e magazzino dal 24 Dicembre al 06 Gennaio. Gli ordini effettuati in queste date verranno elaborati a partire dal 07 Gennaio 2025.

PROMOZIONI attive  Italiano  Filamenti KIMYA  |  Bambu Lab X1E Bundle  |  Stampanti 3D UltiMaker e Raise3D

Offices and warehouse closure from December 24th to January 6th. Orders placed on these dates will be processed starting from 07 January 2025.

Active PROMOTIONS  English  KIMYA Filaments  |  Bambu Lab X1E Bundle  |  UltiMaker and Raise3D 3D printers

Cierre de oficinas y depósitos del 24 de Diciembre al 6 de Enero. Los pedidos realizados en estas fechas se procesarán a partir del 7 de enero de 2025..

PROMOCIONES activas  Español  Filamentos KIMYA  |  Bambu Lab X1E Bundle  |  Impresoras 3D UltiMaker y Raise3D

Fermeture des bureaux et de l'entrepôt du 24 Décembre au 6 Janvier. Les commandes passées à ces dates seront traitées à partir du 7 Janvier 2025.

PROMOTIONS actives  Français  Filaments KIMYA  |  Bambu Lab X1E Bundle  |  Imprimantes 3D UltiMaker et Raise3D

Schließung von Büro und Lagerhalle vom 24. Dezember bis 6. Januar. An diesen Terminen aufgegebene Bestellungen werden ab dem 7. Januar 2025 bearbeitet.

Aktive WERBEAKTIONEN  Deutsch  KIMYA-Filamente  |  Bambu Lab X1E Bundle  |  UltiMaker und Raise3D 3D-Drucker

Bambu PLA-CF | 1.75mm | 1Kg

32.76 €
Not Rated
paga in 3 rate con Klarna
pay in 3 with Klarna
paga en 3 plazos con Klarna
payez en 3 fois avec Klarna
Zahlen Sie in 3 Raten mit Klarna
prodotto presente su  Crea3D è presente su MEPA
Color
Weight

Volume discounts

QuantityPriceYou Save
431.12 €Up to 6.55 €
829.48 €Up to 26.21 €
1227.85 €Up to 58.97 €
In Stock

Bambu PLA-CF

Bambu PLA-CF is carbon fiber reinforced PLA with improved stiffness and strength. PLA-CF is easy to print and beginner-friendly like regular PLA. It is AMS compatible with low clogging risk at high-speed printing. The prints are in matte finish with almost invisible layer lines, which make it suitable for printing general engineering parts or models requiring a better appearance, like bike frames, brackets and toys.

 

Carbon fiber texture & Minimized layer lines

The addition of carbon fiber gives prints a unique matte finish and effectively hides layer lines, providing a smooth, premium look.

 

 

Display of Prints

Bambu PLA-CF could be paired with any PLA series filament to make your prints more colorful and achieve various texture requirements.

 

 

Mechanical Properties Comparison

 

PLA Matte PLA-CF Improved %
Tensile Strength - XY/MPa 32 38 19%
Tensile Strength - Z/MPa 25 26 4%
Bending Strength - XY/MPa 53 89 68%
Bending Strength - Z/MPa 32 49 53%
Bending Modulus - XY/MPa 2360 3950 67%
Bending Modulus - Z/MPa 2040 2260 10%
Impact Strength - XY/(kJ/m²) 19.2 23.2 20%
Impact Strength - Z/(kJ/m²) 6.6 7.8 18%

 

 

Stablized printing dimension

Bambu PLA-CF features low shrinkage and warping resistance to achieve a perfect matching accuracy between prints parts.

 

 

Minimal effort in support removal

Bambu PLA-CF is designed to support itself. It can be removed more easily compared to regular PLA, and still maintains a smooth support surface.

 

 

Not prone to clogging in high-speed printing

Bambu PLA-CF is just as easy to print as regular PLA. It can be printed smoothly and consistently at high speed without clogging.

 

 

RFID for Intelligent Printing

All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System). Load and print! No more tedious setting steps.

 

A50-K0-1.75-1000-SPL

Download


Recommended Printing Settings
Drying Settings (Blast Drying Oven) 55 °C, 8 h
Printing and Keeping Container's Humidity < 20% RH (Sealed, with Desiccant)
Nozzle Temperature 210 - 240 °C
Bed Temperature (with Glue) 35 - 45 °C
Printing Speed < 200 mm/s

 

Physical Properties
Density 1.22 g/cm³
Vicat Softening Temperature 69 °C
Heat Deflection Temperature 55 °C
Melting Temperature 165 °C
Melt Index 3.7 ± 0.6 g/10 min

 

Mechanical Properties
Tensile Strength 38 ± 4 MPa
Breaking Elongation Rate 8.4 ± 3.2 %
Bending Modulus 3950 ± 190 MPa
Bending Strength 89 ± 4 MPa
Impact Strength 23.2 ± 3.7 kJ/m²