Addigy® PA6/66-GF20 FR LS is a newly developed flame retardant material that is compliant with EN 45545-2, NFPA 130 (ASTM E162, ASTM E662) and SMP 800-C. This material was designed specifically for 3D printing to achieve ideal mechanical properties with excellent flame retardancy, low smoke and low toxicity. The material is ideal for the production of end use parts using printers with enclosed or heated chambers.

Benefits
  • Flame retardant material
  • Semi-crystalline thermoplastic
  • Good impact strength and stiffness
  • Good low temperature properties (e.g. -40°C)
  • Outstanding wear resistance
  • Good temperature resistance
  • Reduced thermo-oxidative degradation
  • Improved long term heat and stability to ultraviolet and visible light

Applications*
  • Functional end use parts
  • Functional prototypes
*Subject to detailed product specifications.

Color
  • Black

Printing Parameters

  • Print Temperature = 230-250°C
  • Print Speed = 20-50 mm/s
  • Bed Adhesion = Magigoo PA
  • Bed Temperature = 80°C
  • Fan Settings = off to low
  • Nozzle = use of a fiber capable nozzle (e.g. hardened steel, ruby)
16136297
Property  Typical Values Units Test Method Test Specimen
   black natural       
MECHANICAL PROPERTIES          
Tensile stress at yield, 50 mm/min     MPa ISO 527 Injection molded
    -- MPa ISO 527 3D printed XY / flat at 240°C
at -40°C   -- MPa ISO 527 3D printed XY / flat at 240°C
    -- MPa ISO 527 3D printed XZ / on edge at 235°C
      MPa ISO 527 3D printed ZX / upright at 235°C
Tensile stress at break, 50 mm/min     MPa ISO 527 Injection molded
  46 MPa ISO 527 3D printed XY / flat at 240°C
at -40°C   52 MPa ISO 527 3D printed XY / flat at 240°C
    53 MPa ISO 527 3D printed XZ / on edge at 235°C
      MPa ISO 527 3D printed ZX / upright at 235°C
Tensile elongation at yield, 50 mm/min   -- % ISO 527 3D printed XY / flat at 240°C
at -40°C   -- % ISO 527 3D printed XY / flat at 240°C
    -- % ISO 527 3D printed XZ / on edge at 240°C
      % ISO 527 3D printed ZX / upright at 240°C
Tensile elongation at break, 50 mm/min     % ISO 527 Injection molded
    2.5 % ISO 527 3D printed XY / flat at 240°C
at -40°C   2.1 % ISO 527 3D printed XY / flat at 240°C
    1.7 % ISO 527 3D printed XZ / on edge at 240°C
    % ISO 527 3D printed ZX / upright at 235°C
Tensile modulus (modulus of elasticity), 1 mm/min     MPa ISO 527 Injection molded
  3999 MPa ISO 527 3D printed XY / flat at 240°C
at -40°C   4056 MPa ISO 527 3D printed XY / flat at 240°C
    4876 MPa ISO 527 3D printed XZ / on edge at 240°C
      MPa ISO 527 3D printed ZX / upright at 235°C
Flexural modulus   5588 MPa ISO 178 Injection molded
Flexural strength   147 MPa ISO 178 Injection molded
Izod impact notched     MPa ISO 180 Injection molded
Charpy impact notched     MPa ISO 179 Injection molded
  13.1 MPa ISO 179 3D printed XY / flat at 240°C
FLAMMABILITY PROPERTIES        
UL 94 flammability rating V-2 at 0.4 mm V-2 at 0.4 mm UL 94 3D printed XY / flat at 240°C
  V-2 at 0.8 mm  V-2 at 0.8 mm UL 94 3D printed XY / flat at 240°C
  V-1 at 1.6 mm  V-2 at 1.6 mm UL 94 3D printed XY / flat at 240°C
   V-1 at 2.0 mm UL 94 3D printed XY / flat at 240°C
  V-0 at 3.2 mm V-0 at 3.2 mm UL 94 3D printed XY / flat at 240°C
EN 45545-2+A1 NORM      
Oxygen index   33.6 at 4 mm % R22 - EN ISO 4589-2 3D printed XY / flat at 240°C
Smoke production (Ds max)   111.1 at 4 mm R22 - EN ISO 5659-2, 25 kW/m2 3D printed XY / flat at 240°C
ITCPNL   0.51 at 4 mm NF X 70-100-1, NF X 70-100-2, 600°C 3D printed XY / flat at 240°C
      3D printed XY / flat at 240°C
      3D printed XY / flat at 240°C
NFPA 130 NORM          
Radiant panel index (Is)   8 at 6 mm   ASTM  E162-15b 3D printed XY / flat at 240°C
Optical density at 4 minutes (Ds)   94 at 6 mm   ASTM E662-18 3D printed XY / flat at 240°C
        3D printed XY / flat at 240°C
Toxic gas generation   pass   Bombardier SMP 800-C 3D printed XY / flat at 240°C
FAR 25.853 NORM          

Burn length

   20.3 (0.8) mm (") Vertical test – 12 seconds, FAR 25.853 3D printed XY / flat at 240°C

Flame time

   6.1 s

Vertical test – 12 seconds, FAR 25.853

 3D printed XY / flat at 240°C

Flaming time of drippings

   0.0 s Vertical test – 12 seconds, FAR 25.853 3D printed XY / flat at 240°C

Burn rate

   n/a (< 38.1 ( 1.5)) mm/min (in/min) Horizontal test – 12 seconds, FAR 25.85 3D printed XY / flat at 240°C
THERMAL PROPERTIES          
Melting point   195 °C ISO 11357, DSCb  
Glass transition temperature   °C ISO 11357, DSCb  
Heat deflection temperature at 1.8 MPa (A)     °C ISO 75 Injection molded
    114 °C ISO 75 3D printed XY / flat at 240°C
Heat deflection temperature at 0.45 MPa (B)     °C ISO 75 Injection molded
    168 °C ISO 75 3D printed XY / flat at 240°C
GENERAL PROPERTIES          
Density   1293 kg/m3 ISO 1183  
pH 4.3 4.5     1% in H2O
Water absorption     % ISO 62 24 hours at 23°C
Water content - coulometric Karl Fischer     μg/g ISO 12937  
Water content   %
 ISO 15512 after drying at 120°C for 2 hours
non-volatile-matter content   ~30 % ISO 3251  