- Prezzo scontato
Kimya PLA-R
19.20 €
IVA esclusa
PLA-R 3D Filament
The 3D filament Kimya PLA-R is a recycled and biodegradable polymer: this biosourced homopolymer can be obtained from corn starch.
fai acquisti fino a 3.000€ e paga in 3 rate con 
buy up to €3.000 and pay in 3 with
prodotto presente su 
The 3D filament Kimya PLA-R is a recycled and biodegradable polymer: this biosourced homopolymer can be obtained from corn starch. Polylactic acid (PLA) is a natural alternative to polyethylene. It is easy to print and is odorless.
The 3D filament Kimya PLA-R can be used in industrial applications, notably packaging, and also in domestic applications: creation of everyday objects, toys, prototypes and for use in modeling.
It offers the following properties:
- Easy to print
- Odorless
- Glossy finish
- ≥ 97% recycled materials (100% recycled materials – PLA-R Natural)
- Eligible to the EN 13432 and EN 14995 standards (PLA-R Natural)
- Complies with the REACH standard
PL1106OW
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
| Density | ISO 1183-1 | 1.24 g/cm3 |
| Moisture rate | INS-6711 | < 1 % |
| Melt flow index (MFI) | ISO 1133-1 (@210°C – 2,16 kg) | 9 - 12 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-220°C) | 61 °C |
| Melting Temperature (Tm) | ISO 11357-1 DSC (10°C/min – 20-220°C) | 150 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 40-150 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 190-210°C |
| Bed T° | 20-60°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/5A/50 | 2,963 MPa |
| Tensile Strength | ISO 527-2/5A/50 | 57.9 MPa | |
| Tensile strain at strength | ISO 527-2/5A/50 | 2.2 % | |
| Tensile Stress at Break | ISO 527-2/5A/50 | 47.3 MPa | |
| Tensile strain at break | ISO 527-2/5A/50 | 4 % | |
| Flexural modulus | ISO 178 | 2,675 MPa | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 88.8 MPa | |
| Flexural stress at break | ISO 178 | 91.6 MPa | |
| Charpy impact resistance | ISO 179-1/1eA | 3.22 kJ/m² | |
| Shore Hardness | ISO 868 | 79.1D |
| Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 | The data should be considered as indicative values - Properties can be influenced by production conditions. |
Created on 07/01/2018 - Revised on 01/07/2019.
Potrebbero anche piacerti
- Prezzo scontato
I clienti che hanno acquistato questo prodotto hanno comprato anche:
- Prezzo scontato
PLA-R 3D Filament
The 3D filament Kimya PLA-R is a recycled and biodegradable polymer: this biosourced homopolymer can be obtained from corn starch.
Nessuna recensione per il momento.