LUVOCOM 3F PAHT CF 9891 BK

LUVOCOM 3F PAHT CF 9891 BK | 750g

88.00 €

LUVOCOM 3F PAHT® CF 9891 BK is a high-temperature, carbon fiber-reinforced, polyamide-based material. It provides high strength, stiffness, and minimized water uptake.

prodotto presente su

Diametro

1.75 mm
2.85 mm

Disponibile

LUVOCOM 3F high-performance materials are optimized for industrial 3D printing. They enable quality controlled additive manufacturing of end-use parts. LEHVOSS materials are certified quality, and exhibit high mechanical strength.

LUVOCOM 3F PAHT® CF 9891 BK is optimized for industrial additive manufacturing and prints perfectly on all known filament printers.

Main benefits:

Easy to print
No warping
Very high mechanical strength and stiffness
Quality print surface

Main properties:

Tensile strength up to 130 MPa
Temperature resistant up to 150°C
Low water uptake
It is compatible for dual extrusion with the following materials: PVOH and HIPS

Riferimento 16134220

Scarica

GENERIC MACHINERY SETTINGS
The following settings are a generic guide, geometrical requirements of the application or the used printer could make necessary to adjust this values to obtain the best result. These generic settings are stablished for a 0.6mm Nozzle Diameter and a Glass Build Plate surface, note that for different nozzle diameters and/or a different build plate surface material, the settings should be changed accordingly.

Print speed: 40-60 mm/s
Layer Height: >0.2 mm
Brim/Skirt: 15 outlines with 1 layer
Extrusion temperatures: Range of nozzle temperatures (265-290ºC / 509-554ºF).
Build plate temperature: >50ºC / 122ºF
Build plate adhesion: We recommend to an adhesive promotor. Adding a (large) skirt/brim to the print will help in stablishing build plate adhesion during the print as well.
Cooling Fan: Off

MATERIAL HANDLING
Store: In order to prevent moisture pick up and contamination, supplied packaging should be kept closed and undamaged. For the same reason, partially used bags should be sealed before re-storage.
Allow the material that has been stored elsewhere to adapt to the temperature in the processing room while keeping the bag closed.
Packaging: LUVOCOM 3F Filament is supplied in cardboard box, spools packed in vacuumed polymer/aluminum film.
It is advisable to predry the filament with a suitable dryer for optimal performance.

NOTE: When melted, LUVOCOM 3F PAHT® CF 9891 filament can be abrasive due to its carbon reinforcement. Printing with LUVOCOM 3F PAHT® CF 9891 may reduce brass nozzles and extruder driving wheels lifetime. For a better experience, using hardened steel nozzles and extruder driving wheels is advised.